Preparation before MIG weld aluminum for robot welding aluminum
How to clean the base metal and welding wire before MIG welds aluminum?
Aluminum and aluminum alloy weldments should be cleaned before welding. The purpose is to remove oxide film and oil to prevent stomata and slag from forming in the weld.
The cleaning methods commonly used in production include two processes of cleaning oil and removing oxide film.
1. Cleaning of oil stains
The oil stain on the surface of the workpiece can be wiped with gasoline, carbon tetrachloride, trichloroethylene and acetone. When cleaning, it should be cleaned with a clean white cloth and solvent. Be careful not to use cotton yarn.
2. Cleaning of the oxide film
The surface oxide film is ineffective by the above solvent cleaning, and only chemical cleaning and mechanical cleaning can be used.
a. Chemical cleaning is to clean the surface of the workpiece with alkali and acid. The method can remove the oxide film and remove the oil. The specific process is as follows: sodium hydroxide solution with a volume fraction of 6% to 10%, soaked at 70 ° C or so. 0.5min → water washing → 15% nitric acid soaked at room temperature for 1min for neutralization treatment → water washing → warm water washing → drying. The surface after washing is a matt silver white.
b. Mechanical cleaning can use pneumatic or electric milling cutters, and tools such as scrapers and boring tools can also be used. For thinner oxide films, stainless steel wire brushes or thin wire brush brushes can also be used until a metallic luster is exposed.
It is best to apply welding immediately after cleaning. If the parking time exceeds 4h, it should be cleaned up again.
It is more important for wire cleaning. The supply of the wire shall be a clean and brightly treated coiled wire, usually in a plastic bag. It should be used up as soon as possible after opening. Otherwise the contaminated wire is difficult to reuse.
Robot welding aluminum specification
|Robot model||ZK1400 - 06|
|Mounting||Vertical ground installation, lifting, hanging|
|Number of axes||6|
|Max working radius||1400mm|
|Repeated posiontioning accuracy||0.03mm|
|Maximum joint range||J1||RV reducer ±160°|
|J2||RV reducer +110°, -70°|
|J3||RV reducer +65°, -120°|
|J4||RV reducer ±150°|
|J5||Hollow harmonic reducer +105°, -110°|
|J6||Hollow harmonic reducer ±320°|
|Maximum joint speed||J1||RV reducer 201.9°/S|
|J2||RV reducer 198.3°/S|
|J3||RV reducer 198.3°/S|
|J4||RV reducer 296.2°/S|
|J5||Hollow harmonic reducer 197.5°/S|
|J6||Hollow harmonic reducer 247.2°/S|
|Allowable bending moment N.m||J4||RV reducer 9.8N.m|
|J5||RV reducer 9.8N.m|
|J6||Hollow harmonic reducer 4N.m|
|Allowable inertia Kg.㎡||J4||RV reducer 0.3kg.㎡|
|J5||RV reducer 0.3kg.㎡|
|J6||Hollow harmonic reducer 0.05kg.㎡|
|Body total weight||KG||185KG|
|Operating environment||Temperature||0℃ - 45℃|
|Humidity||20% - 80%|
Keep away from corrosive gases or liquids or explosive gases,
|Power capacity||6KVA (Robot) + 24KVA (Welding source )|
Manufactor of robot welding aluminum
Welding positioner of robot welding aluminum
Contact Person: Daisy He